Plasma-Induced Formation of Pt Nanoparticles with Optimized Surface Oxidation States for Methanol Oxidation and Oxygen Reduction Reactions to Achieve High-Performance DMFCs.

Plasma treatment and reduction are used to synthesize Pt nanoparticles (NPs) on nitrogen-doped carbon nanotubes (p-Pt/p-NCNT) with a low Pt content. In particular, the plasma treatment is used to treat the NCNT to give it with more surface defects, facilitating a better growth of the Pt NPs, while the plasma reduction produces the Pt NPs with a reduced fraction of the surface atoms at the high oxidation states, increasing the catalytic activities of the p-Pt@p-NCNT. Even at the low Pt content (7.8 wt.%), the p-Pt@p-NCNT shows superior catalytic activities and good stabilities for methanol oxidation reaction (MOR) and oxygen reduction reaction (ORR). The density functional theory (DFT) calculations indicate that the defects generated in the plasma treatment can help the growth of the Pt NPs on the NCNTs, leading to the stronger electronic coupling between Pt and NCNT and the increased stability of the catalyst. The plasma reduction can give the Pt NPs with optimized surface oxidation states, decreasing the energy barriers of the rate-determining steps for MOR and ORR. When used as the anode and cathode catalysts for the direct methanol fuel cells (DMFCs), the p-Pt@p-NCNT exhibits a higher maximum power density of 81.9 mW cm-2  at 80 °C and shows good durability.

Construction of Co/FeCo@Fe(Co)3O4 heterojunction rich in oxygen vacancies derived from metal-organic frameworks using O2 plasma as a high-performance bifunctional catalyst for rechargeable zinc-air batteries.

Developing high-efficient, good-durability, and low-cost bifunctional non-precious metal catalysts for both oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) is urgent and significant for promoting the practical rechargeable zinc-air batteries (RZABs). Herein, N-doped carbon coated Co/FeCo@Fe(Co)3O4 heterojunction rich in oxygen vacancies derived from metal-organic frameworks (MOFs) is successfully constructed by O2 plasma treatment. The phase transition of Co/FeCo to FeCo oxide (Fe3O4/Co3O4) mainly occurs on the surface of nanoparticles (NPs) during the O2 plasma treatment, which can form rich oxygen vacancies simultaneously. The fabricated catalyst P-Co3Fe1/NC-700-10 with optimal O2 plasma treatment time of 10 min can reduce the potential gap between the OER and ORR to 760 mV, which is much lower than commercial 20% Pt/C + RuO2 (910 mV). Density functional theory (DFT) calculation indicates that the synergistic coupling between Co/FeCo alloy NPs and FeCo oxide layer can promote the ORR/OER performance. Both liquid electrolyte RZAB and flexible all-solid-state RZAB using P-Co3Fe1/NC-700-10 as the air-cathode catalyst display high power density, specific capacity and excellent stability. This work provides an effective idea for the development of high performance bifunctional electrocatalyst and the application of RZABs.